316Ti is a titanium stabilized version of 316 molybdenum-containing austenitic stainless steel. It is more resistant to general corrosion and pitting/crevice corrosion than traditional chromium-nickel austenitic stainless steels such as 304.

316L stainless steel features a lower proportion of carbon in its composition. The amount of carbon cannot be higher 0.03%. This lowers the risk of carbon precipitation, making it a better option for welding to achieve maximum corrosion resistance.

304L stainless steel is remarkably similar to 304 stainless steel in their chemical composition with one key difference. the maximum carbon of 304L stainless steel content is set at 0.08%, whereas grade 304L stainless steel has a maximum carbon content of 0.03%. This is why the “L” in 304L can be interpreted as extra-low carbon. It is widely used in the production of equipment and parts that demand better corrosion

304 stainless steel is a superior material with regard to corrosion resistance, heat resistance, low temperature strength and mechanical properties, as one of the most widely used types of stainless steel. In addition, it has exceptional hot-workability such as stamping and bending, without leaving heat treatment hardening phenomenon.

310S stainless steel is austenitic chromium-nickel stainless steel, with good oxidation resistance, corrosion resistance, because of a higher percentage of chromium and nickel, so that it has much better creep strength, with good high temperature resistance.

316 stainless steel also contains 2-3% molybdenum, in addition to iron, chromium and nickel. The addition of molybdenum significantly improves the performance of 316 stainless steel in certain corrosive environments, especially those containing chlorides. 316 stainless steel is more commonly used in situations requiring higher corrosion resistance.

201 stainless steel generally refers to 201 stainless steel and acid resistant steel. 201 stainless steel refers to the steel that is resistant to the corrosion of weak media such as atmosphere, steam and water, while acid resistant steel refers to the steel that is resistant to the corrosion of chemical corrosive media such as acid, alkali and salt.

2507 duplex stainless steel is a special ferritic-austenitic duplex stainless steel with excellent corrosion resistance. It achieves comprehensive protection against point corrosion, crevice corrosion and uniform corrosion through the ratio of chromium and molybdenum elements.

201 stainless steel generally refers to 201 stainless steel and acid resistant steel. 201 stainless steel refers to the steel that is resistant to the corrosion of weak media such as atmosphere, steam and water, while acid resistant steel refers to the steel that is resistant to the corrosion of chemical corrosive media such as acid, alkali and salt.

310S stainless steel is austenitic chromium-nickel stainless steel, with good oxidation resistance, corrosion resistance, because of a higher percentage of chromium and nickel, so that it has much better creep strength, can continue to work at high temperatures, with good high temperature resistance.

440C stainless steel is a high carbon martensitic stainless steel. It has high strength, moderate corrosion resistance, and good hardness and wear resistance. Grade 440C is capable of attaining, the highest strength, hardness and wear resistance of all the stainless alloys after heat treatment

2205 Duplex stainless steel alloy is a duplex stainless steel composed of 22% chromium, 2.5% molybdenum and 4.5% nickel nitrogen alloy. It has high strength, good impact toughness and good overall and local resistance to stress corrosion.